J. Kawamura et al., INTERMEDIATE RANGE STRUCTURE OF ORGANIC-INORGANIC MIXED SUPERIONIC CONDUCTOR GLASSES - AGI AND TETRAALKYLAMMONIUM IODIDES, Solid state ionics, 86-8, 1996, pp. 517-520
Intermediate range structures of organic-inorganic mixed superionic co
nductor glasses were investigated by low-angle neutron diffraction and
small-angle neutron scattering (SANS) experiments. Significant small
angle scatterings were observed in the glasses composed of AgI-CsI-deu
terized-tetramethylammonium iodides. The fractal dimension D-f was est
imated from the plot of the log I(q) vs. log q; it was 0.39 above q(c)
and 2.8 below, where q(c) was a cross-over wavelength of q(c) similar
to 0.02-0.05 Angstrom(-1). This result strongly supports the existenc
e of percolation clusters in the organic-inorganic mixed superionic co
nductor glasses, which has been expected from ionic conductivity measu
rements.