HEAT-CAPACITY OF TERNARY COMPOUNDS RNIGE(R=GD,DY,ER, AND Y)

The heat capacity of the ternary compounds RNiGe(R=Er, Dy, Gd, and Y) was studied in the temperature range between 2 and 40 K. From the heat capacity curves, Neel temperatures are found to be 3.3, 7.4, and 10.7 K for ErNiGe, DyNiGe, and GdNiGe, respectively. The heat capacity of YNiGe was well fitted with an average Debye temperature of 272 K in th e temperature range between 2 and 40 K. The changes of magnetic entrop y indicate a strong influence of the crystal field on the Er+3 and Dy3 ion in ErNiGe and DyNiGe compounds. These results suggest the possib ility of using these compounds as magnetic regenerator materials near the temperature of 4.2 K. (C) 1995 American Institute of Physics.