GIANT MAGNETOSTRICTION IN AMORPHOUS (TB1-XDYX)(FE0.45CO0.55)(Y) FILMS

The magnetization and magnetostriction have been studied in amorphous (Tb1-xDyx)(Fe0.45Co0.55)(y) films. A well-defined easy axis is created by magnetic field annealing and the sperimagnetic cone structure, cha racteristic of these amorphous alloys, is reduced. The anisotropy has a minimum at x = 0.73 as in the R Fe-2 Laves phase. This points to the similarity between the local environments in the amorphous and crysta lline states. A giant magnetoelastic coupling coefficient b of 60 MPa is developed at 300 K in low applied field for x = 0, optimally anneal ed films. Assuming a Young's modulus and a Poisson ratio of 80 GPa and 0.31, respectively, the magnetostriction is evaluated at 1020 x 10(-6 ). This is much larger than previously reported values in other amorph ous films. (C) 1996 American Institute of Physics.