T. Yoshitake et al., INTERMODULATION DISTORTION MEASUREMENTS OF A MICROSTRIP BAND-PASS FILTER MADE FROM DOUBLE-SIDED YBA2CU3OX, FILMS, Applied physics letters, 67(26), 1995, pp. 3963-3965
A microstrip three-pole band-pass filter, with a midband frequency of
9.5 GHz and a fractional bandwidth of 2%, has been fabricated using do
uble-sided YBa2Cu3Ox (YBCO) films on MgO substrates. The nonlinear beh
avior of this filter was studied by intermodulation distortion measure
ments. The insertion loss at the midband frequency was less than 0.1 d
B and the return loss was better than 15 dB throughout the passband at
55 K. This filter showed relatively high power handling capabilities,
with third-order intercept larger than +60 dBm at 55 K. The third-ord
er intermodulation distortion products of this filter were found to va
ry with frequency in the passband, being larger near each of the band
edges than at the midband. These increases in the nonlinearity near th
e band edges are attributed to the increase in the average stored ener
gy in the filter, which is confirmed by the increase in the group dela
y near the band edge. (C) 1995 American Institute of Physics.