J. Sommer et al., SILVER TRACER DIFFUSION IN ORIENTED AG CU INTERPHASE BOUNDARIES AND CORRELATION TO THE BOUNDARY STRUCTURE/, Acta materialia, 44(1), 1996, pp. 327-334
Citations number
30
Categorie Soggetti
Material Science","Metallurgy & Metallurigical Engineering
Radiotracer experiments were performed on oriented Ag/Cu bicrystals to
study the influence of the interphase boundary (IB) structure on the
material transport along the interfaces. Tracer diffusion of Ag-100m w
as measured along (011) IBs in the [100] and [01(1) over bar] directio
ns and along (111) IBs in the [01(1) over bar] and [<(2)over bar 11>]
directions in the temperature range 593-882 K. It is demonstrated for
cube-on-cube orientations how the interfacial structure is reflected i
n the diffusion behavior. It was found that the Ag diffusion along ani
sotropic misfit dislocation arrays in (011) IBs is anisotropic and fas
test along channels of rapid diffusion. A scatter in the diffusion dat
a for (011) IBs indicates that their structure, quite in contrast to m
orphologically stable (111) interfaces, depends on the thermal history
of the specimens. This is interpreted as a result of microfaceting of
the morphologically unstable (011) IBs. Furthermore, the influence of
interdiffusion across the interface on the diffusion along the interf
ace is discussed.