S. Hariprasad et al., DEFORMATION-BEHAVIOR OF A RAPIDLY SOLIDIFIED FINE-GRAINED AL-8.5-PERCENT-FE-1.2-PERCENT-V-1.7-PERCENT-SI ALLOY, Acta materialia, 44(1), 1996, pp. 383-389
Citations number
17
Categorie Soggetti
Material Science","Metallurgy & Metallurigical Engineering
Deformation characteristics of a rapidly solidified dispersion strengt
hened Al-8.5% Fe-1.2% V-1.7% Si alloy processed by planar dow casting
was studied by tension testing at 25-420 degrees C, compression testin
g at 25 degrees C and hardness tests. The as-processed alloy shows non
-linear elastic behavior, yield drop,low uniform and total elongation,
serrated yielding, stress relaxation, flow softening and anomalous st
rain rate dependence of ductility. The results indicate that greater d
ynamic recovery due to fine grains (<0.3 mu m) and essentially pure al
uminum matrix in the as-processed planar flow cast alloy contribute to
the observed deformation characteristics. Corroborative evidence for
the recovery processes was obtained by differential scanning calorimet
ry and hardness measurements of cold rolled and annealed samples.