The magnetic properties of Y(Co1-xFex)(10)Si-2 (x = 0.0, 0.2, 0.4, 0.6
, 0.8, 1.0) compounds have been studied. All compounds crystallize in
ThMn12 type structures. The lattice parameters a and c increase with i
ncreasing iron content, while the Curie temperature has a maximum at a
bout x = 0.6. The easy magnetization direction at room temperature cha
nges from basal plane to the c-axis at about x = 0.2. The anisotropy f
ield obtained by the SPD technique reaches a maximum at x = 1.0, with
values of 2.1 T at room temperature and 2.6 T at 77 K respectively.