The possibility of fabrication of diamond-like coating on high-ir, sup
erconductors is investigated. Carbon thin films were deposited on sing
le-crystal YBa2Cu3O7 film substrates by pulsed-laser sputtering of gra
phite targets. Deposition at room temperature yields diamond-like film
s with high optical transmission, high resistivity, and good adhesion
to unpretreated substrates. Degradation of superconducting properties
or deterioration of mechanical characteristics of YBa2Cu3O7 films was
not observed after carbon deposition and subsequent low-temperature th
ermocycling. The water-protective properties of these diamond-like coa
tings were investigated.