New structural results of the epitaxial growth of Co/Cu(111) in the co
verage regime 1.5-15 ML are presented as investigated by quantitative
LEED and STM. In the low coverage regime there is pure fee stacking wi
th copper diffused on top of 30% of the domains. The growth is ideally
pseudomorphic. At intermediate coverages hcp stacked domains develop
on the cost of fee domains whereby the latter seem to be stabilized by
their top copper layer. At high coverages the film is predominantly h
cp exhibiting the ideal lattice parameter of Co(0001).