C. Moreau et al., HIGH-TEMPERATURE BEHAVIOR OF THERMOELECTRIC-POWER OF IMPLANTED POLYMER-FILMS, Radiation effects and defects in solids, 137(1-4), 1995, pp. 1355-1360
The results of thermopower S measurements performed on implanted polyp
araphenylene and polyimide films between 150 K and 450 K are presented
. The implantations of Caesium or Iodine ions in polyparaphenylene wit
h low parameters induce a sign of S characteristic to chemical nature
of the implanted ions and an increase of \S\ at around 350 K due to a
transition from a VRH process to a polaronic conduction. With Iodine i
mplanted sample at higher energy (E = 250 keV) and low dose (D = 2 x 1
0(15) ions/cm(2)) a transition from p type to n type doping at 400 K i
s attributed to a migration of negative oxygen ions as in the case of
polyimide samples implanted with Caesium and Iodine ions where a simil
ar behaviour of S is found.