The linear thermal expansion of the bulk amorphous Zr41.2Ti13.8Cu12.5N
i10Be22.5 (atomic percent) alloy has been measured from 80 K to 773 K,
The data for T < T-g were fitted by a model based on the Gruneisen re
lation and a Debye expression for the heat capacity. From the fit, we
deducted the Gruneisen parameter, gamma = 1.25, and the Debye temperat
ure, Theta(D) = 400 K. Annealing the amorphous alloy at 663 K, which i
s between the glass transition temperature T-g = 623 K, and the crysta
llization temperature T-x = 693 K, causes viscous flow in the sample.
This is due to the small viscosity in the undercooled liquid.