A new polymer of polyester derivative (PE) blend with poly(N-vinycarba
zole) (PVK) and compound of PBD at various weight ratio were used as e
mitter in unilayer electroluminescence (EL) devices with indium cathod
e. Analyses of fluorescence and EL spectra imply common emission energ
y states are formed in the blend films, by which to explain the possib
ility of maximum EL efficiency in blend films higher than that in eith
er of PE and PVK. The PL and EL spectra show the maximum emission band
shifts red slightly between 430 nm and 450 nm as increasing the ratio
of PE, meanwhile the half width increases and a new peak around 525 n
m appears. The new peak is confirmed originating from the dimer formed
by coupling of interchains in polymer PE. Both of PE and PVK can give
rise to PL emission under UV light. The origin of PC and EL emission
is analysed.