Upon sputtering and subsequent annealing, the subsurface region of the
(100) surface of FeAl undergoes a transition to a practically stable
and ordered Fe3Al slab. It is capped by an Al top layer forming a rath
er complex interface to the bulk FeAl. This shows that routine surface
preparation procedures with sputtering involved can lead to substanti
al restructuring extending deep into the surface.