MAGNETOSTRICTION HYSTERESIS LOOPS OF ANNEALED FE73.5CU1NB3SI15.5B7 METALLIC-GLASS STRIPS

Authors
KACZKOWSKI Z RUUSKANEN P
Citation
Z. Kaczkowski et P. Ruuskanen, MAGNETOSTRICTION HYSTERESIS LOOPS OF ANNEALED FE73.5CU1NB3SI15.5B7 METALLIC-GLASS STRIPS, Journal of magnetism and magnetic materials, 158, 1996, pp. 201-202
Citations number
12
Categorie Soggetti
Material Science","Physics, Condensed Matter
Journal title
Journal of magnetism and magnetic materials → ACNP
ISSN journal
03048853
Volume
158
Year of publication
1996
Pages
201 - 202
Database
ISI
SICI code
0304-8853(1996)158:<201:MHLOAF>2.0.ZU;2-E
Abstract
Magnetostriction hysteresis loops of Fe73.5Cu1Nb3Si15.5B7 metallic gla ss strips annealed in vacuum for 1 h at temperatures ranging from 300 to 650 degrees C were determined using a strain-gauge method. The magn etostriction at H-m = 2.8-3.0 kA/m decreased from 25 x 10(-6) after an nealing at 300 degrees C to 21 x 10(-6) after annealing at 560 degrees C, to about 2 x 10(-6) after annealing at 600 degrees C, and increase d to approximately 6 x 10(-6) after annealing at 650 degrees C. The re manent magnetostriction after annealing from 300 to 560 degrees C incr eased from 1.35 x 10(-6) to 5.01 x 10(-6).