Thermomagnetic curves of rapidly solidified ribbons of Fe-3.5 wt% Si p
repared using the single wheel and double roller techniques are discus
sed in comparison with those of commercial grain oriented transformer
sheet samples. It is concluded that the arrangement of defect clusters
or silicon or impurity atoms, fixed at the temperature of secondary r
ecrystallization, influence the distribution of magnetic moments at hi
gh temperature.