S. Fomine et al., SYNTHESIS AND CHARACTERIZATION OF NOVEL POLYESTERS AND POLYURETHANES CONTAINING 9,10-DIETHYNYLANTHRACENE AND PYROMELLITIC DIIMIDE, Polymer Journal, 28(8), 1996, pp. 641-646
A Novel monomer 9,10-bis(4-hydroxy-1-butynyl)anthracene (M1) was synth
esized and some polyesters and polyurethanes containing a donor 9,10-d
iethynylanthracene and acceptor pyromellitic diimide groups were prepa
red. The polymers were soluble in common organic solvents and gave tra
nsparent films by casting. They showed 5% weight loss at the temperatu
re 250-300 degrees C. All polymers showed luminescence and maximum dep
ended on polymer composition. Polymers containing the 9,10-diethynylan
thracene moiety alone showed luminescence with maximum at 470-480 nm w
hile those containing 9,10-diethynylanthracene and pyromellitic diimid
e groups showed luminescence with maximum around 600 nm due to the cha
rge transfer complex (CTC) formation between them. Some polymers showe
d electroluminescence with turn-on voltage of 10.5 V.