D. Srinivasan et al., ELECTRICAL-CONDUCTIVITY AND MAGNETORESISTANCE STUDIES ON POLYANILINE-PMMA BLENDS AT VERY-LOW TEMPERATURE, Czechoslovak journal of Physics, 46, 1996, pp. 2035-2036
D.C. electrical conductivity of polyaniline (33%,40%) blended with PMM
A was measured from 5K to 300mK. The conductivity behaviour is consist
ent with fluctuation induced tunneling. Magneto-resistance (MR) was me
asured between 300K and 2K. From 20K to 2K, a large positive MR was ob
served. At 2K, for low magnetic fields (<1 Tesla), a deviation from th
e normal H-2 behaviour was observed.