Te. Warner et al., HIGH-TEMPERATURE IONIC-CONDUCTIVITY IN THE TRIVALENT CERAMIC ELECTROLYTES - LAAL11O18 AND LAAL12O18N, Solid state ionics, 92(1-2), 1996, pp. 99-101
LaAl11O18 and LaAl12O18N which adopt the magnetoplumbite type structur
e were prepared by high temperature sintering techniques from La2O3, a
lpha-Al2O3 and AlN powders. Phase purity was confirmed by powder XRD a
nd IR spectroscopy. Impedance data for ceramic samples with Pt electro
des revealed an intra-granular ionic (La3+) conductivity with activati
on energies E(a)(LaAl11O18) = 2.5 eV and E(a)(LaAl12O18N) = 1.6 eV. At
similar to 1540 K their conductivity is comparable to that for Sr-Li-
beta-alumina with sigma similar to 3 X 10(-5) S cm(-1).