Ba. Vanhassel et al., OXYGEN PERMEATION FLUX THROUGH LA1-YSRYFEO3 LIMITED BY CARBON-MONOXIDE OXIDATION RATE, Applied catalysis. A, General, 119(2), 1994, pp. 279-291
The oxygen permeation flux through La1-ySryFeO3-delta (y = 0.1, 0.2) i
n a large oxygen partial pressure gradient (air/CO, CO2 mixture) was f
ound to be limited by the carbon monoxide oxidation rate at the low ox
ygen partial pressure side of the membrane. The oxygen permeation flux
through the membrane was almost independent of its thickness (1 versu
s 2 mm) and strontium dopant concentration. The deposition of a 50 nm
thin porous platinum layer at the low oxygen pressure side of the memb
rane increased the carbon monoxide oxidation rate and in this way the
oxygen permeation flux by a factor 1.8 +/- 0.2.