PYROELECTRIC SINGLE-ELEMENT AND LINEAR-ARRAY SENSORS BASED ON P(VDF TRFE) THIN-FILMS

The application of pyroelectric poly(vinylidene fluoride/trifluoroethy lene) (P(VDF/TrFE)) copolymer thin films simplifies the manufacture of pyroelectric single-element sensors and, above all, of sensor arrays with high sensitivity, low noise and slight crosstalk. The sensor cons ists of a self-supporting membrane that is a combination of silicon ox ide and silicon nitride. This membrane is made by anisotropic etching on the back of a (100) silicon wafer. Onto the etched wafer a 1-2 mum thin P(VDF/TrFE) film is formed by spin coating. The pyroelectric copo lymer is electrically connected by evaporated electrodes. In this way, both single-element sensors and sensor arrays are produced. Single-el ement sensors built up from P(VDF/TrFE) with a VDF content of 70-80% o n an SiO2/Si3N4 membrane achieve a specific detectivity of up to 3.5 x 10(8) cm square-rootHz W-1 at a modulation frequency of 10 Hz and are temperature stable up to at least 55-degrees-C. For linear arrays noi se-equivalent power (NEP) values of 4.5 and 12 nW have been measured a t chopper frequencies of 40 and 128 Hz, respectively. The average volt age responsivity R(v) (500 K) of P(VDF/TrFE) linear arrays is about 11 0 000 V W-1 at 40 Hz and 40 000 V W-1 at 128 Hz.