Tm. Chen et Lf. Lin, CHEMICAL SYNTHESIS AND CHARACTERIZATION OF SUPERCONDUCTING YBA2CU4O8 AT AMBIENT-PRESSURE, Journal of the Chinese Chemical Society, 41(6), 1994, pp. 735-739
A monophasic high-T-c superconductor YBa2Cu4O8 with T-c(onset) 80 K an
d fme grain size has beeen synthesized under oxygen at 1 bar employing
metal-ethandiol/citric acid (EG/CA) polyester complex precursors. In
addition to the preparation, we report the results of infrared (IR) sp
ectra, thermogravimetric analysis (TGA), and X-ray diffraction (XRD) r
elevant to preparation of the YBa2Cu4O8 superconductor. The effect of
temperature of preparation and precursor compositions (i.e. EG/CA mola
r ratio) on the purity and superconductivity of the YBa2Cu4O8 compound
was investigated. The temperature dependence of resistivity and norma
l-state resistivity of the samples varied systematically with the EG/C
A ratio in the precursors. T-c(onset) and the width of the superconduc
ting transition for YBa2Cu4O8 samples were determined to be 80 K for a
ll samples and 6 - 9 K, respectively; the latter depended on the corre
sponding EG/CA ratios in the precursors. The Meissner fraction of YBa2
Cu4O8 samples determined from dc magnetization tests was independent o
f the EG/CA ratio. Polyester precursors can potentially be applied in
large-scale preparation of high T-c ceramic-oxide superconductors and
superconducting thin firms.