T. Goto et H. Torii, PREPARATION OF LONG Y123 SUPERCONDUCTING FILAMENT BY SOLUTION SPINNING, Journal of low temperature physics, 105(5-6), 1996, pp. 1421-1426
The preparation of a long superconducting Y123 filaments is developed
by using solution spinning for the precursor of the oxide. Long precur
sor filaments are prepared by dry spinning with a starting homogeneous
aqueous PVA solution containing Y, Ba and Cu acetates. The as-drawn f
ilament with 250 mu m in diameter and 300 mm in length is pyrolyzed an
d partial-melted by using a tube furnace with a constant heating zone
of 500 mm. A superconducting filament of 60 mu m in diameter and 200 m
m in length with high J(c) of more than 10(4) A/cm(2) at 77 K and 0 T
is obtained by controlling the partial melting.