MAGNETIC-BEHAVIOR OF THE ALLOYS (CE1-XYX)PDSI3

The results of X-ray diffraction (CuIalpha), electrical resistivity (r ho), heat capacity (C) and magnetic susceptibility (chi) measurements are reported for a new pseudoternary solid solution, (Ce1-xYx)(2)PdSi3 (x = 0.0, 0.2, 0.5, 0.8, 1.0). The X-ray diffraction patterns indicat e that single phase alloys can be formed in a derived version of the A lB2-type hexagonal structure for x greater than or equal to 0.2, while for x = 0.0, apparently there is an additional weak phase. In the cas e of the alloy Ce2PdSi3, the majority of Ce ions do not exhibit magnet ic ordering down to 1.4 K, though magnetic ordering at 7 K from one of the two crystallographically inequivalent sites cannot be ruled out. For other compositions, no magnetic ordering is observed above 1.4 K. The Kondo effect is operative in all these alloys, with the strength o f the Kondo effect increasing with the compression of the lattice by t he gradual replacement of Ce by Y. The C/T exhibits a low temperature enhancement in all Ce containing alloys.