COMPOSITIONAL CHANGE AND COMPOSITIONAL FLUCTUATION IN PB(ZR, TI)O-3 CONTAINING EXCESS PBO

Citation
K. Kakegawa et al., COMPOSITIONAL CHANGE AND COMPOSITIONAL FLUCTUATION IN PB(ZR, TI)O-3 CONTAINING EXCESS PBO, Journal of the American Ceramic Society, 78(4), 1995, pp. 1071-1075
Citations number
12
Categorie Soggetti
Material Science, Ceramics
ISSN journal
00027820
Volume
78
Issue
4
Year of publication
1995
Pages
1071 - 1075
Database
ISI
SICI code
0002-7820(1995)78:4<1071:CCACFI>2.0.ZU;2-C
Abstract
Compositional changes which take place during sintering of Pb(Zr,Ti)O- 3 (PZT) containing excess PbO were studied. The excess PbO forms a liq uid phase during the sintering process, The solubility of the TiO2 com ponent of PZT in liquid PbO is higher than that of ZrO2 component. Thu s, if an excess PbO exists, the composition of PZT phase shifts toward s the Ti-lean side. A change in the lattice constants due to this comp ositional change was actually observed. Coexistence of tetragonal and rhombohedral phases, due to a compositional fluctuation caused by exce ss PbO, was observed near the morphotropic phase boundary, When PZT co ntaining excess PbO was sintered at 1100 degrees C, a compositional fl uctuation occurred early in the process and then decreased with sinter ing time. These phenomena have agreed with a result of computer simula tion of dissolution of TiO2 component in PZT phase into liquid PbO pha se.