Heat capacities have been measured on single crystal specimens of magn
etite containing low levels of Ti or Zn as a replacement for iron. A c
hange in the nature of the Verwey transition from first to second or h
igher order was observed with increasing doping levels. This is in str
ict analogy with prior observations showing a similar change when the
oxygen/iron ratio is increased beyond the 4/3 ratio. The entropy of th
e Verwey transition diminishes with increasing concentration of dopant
s.