M. Kanamaru et al., RADICAL POLYMERIZATION OF VINYL MONOMER HAVING DIACYLUREA MOIETY, Journal of polymer science. Part A, Polymer chemistry, 33(8), 1995, pp. 1361-1365
N-acryloyl-N'-benzoylurea (1) was prepared and its radical homopolymer
ization and copolymerization with styrene were carried out. 1 was synt
hesized yield by the reaction of benzoylisocyanate and acrylamide in t
etrahydrofuran in 78%. Radical polymerization of 1 was carried out at
60 or 80 degrees C in DMF (0.1-2.5M) for 5 h in a sealed tube using AI
BN (3 mol %) or BPO (3 mol %) as initiators to obtain poly(N-acryloyl-
N'-benzoylurea) (2) as a methanol-insoluble part in good yield (75-82%
) independent of concentration. Number-average molecular weights of 2
were 2700-91,900. Furthermore, copolymerization of 1 with styrene was
carried out in various feed ratios to confirm the alternating characte
r in the copolymerization (r(1)r(2) = 0.21) and Q, e values of 1 were
evaluated as 0.52, 1.16, respectively. (C) 1995 John Wiley and Sons, I
nc.