X-RAY STUDY OF FREESTANDING FILAMENT CRYSTALS OF GEXSI1-X SOLID-SOLUTION

In this paper the results of an x-ray study of free-standing filament- like crystals of GexSi1-x solid solution are presented. The crystals w ere grown by a method of vapour transport reactions. The parameter x v aried from 0.004 to 0.271. Independent measurements of both the lattic e parameter and the composition have shown that the lattice parameter of filament crystals with diameters less than 1 mu m is less than that of bulk crystals of the same composition. For example, in the crystal s of 0.5 mu m diameter with x = 0.271 the measured lattice parameter d iffered from its bulk value by 0.0047 Angstrom. The effect is shown to be not connected with high concentrations of impurities of defects. I t is explained by the disturbance of atomic bonds in the uppermost few layers of the crystal and accompanying reconstruction of these layers , which gives rise to a mechanical stress in the crystal bulk. From th ese data the strain decay length was calculated and was found to vary from 10 to 18 Angstrom. The effect observed is unexpectedly large. We connect this value of the observed change with the cylindrical shape o f the crystals. As we did not observe deviations from Vegard's law in the bulk crystals with diameters greater than 1 mu m, we have discusse d the possible origin of such deviations observed by other investigato rs.