Yf. Chang et Jg. Mccarty, ISOTOPIC STUDY OF NOX DECOMPOSITION OVER CU-EXCHANGED OR CO-EXCHANGEDZSM-5 ZEOLITE CATALYSTS, Journal of catalysis, 165(1), 1997, pp. 1-11
The decomposition of NOx over Cu2+- and Co2+-exchanged ZSM-5 zeolites
was investigated using isotope labeled (NO)-N-15-O-18 and temperature-
programmed desorption (TPD) technique. We found that formation of NO2
intermediates is responsible for enhancing the rate of NOx decompositi
on when the catalysts were treated in both (NO)-N-15-O-18 and O-2. Co-
adsorption of (NO)-N-15-O-18 and O-2 led to a dramatic increase in the
amount of NOx and O-2 adsorbed. The surface NOx species decomposed or
desorbed to form NO, O-2, N-2, and NO2 during the TPD. This results i
n formation of equal amounts of (NO)-N-15-O-16 and (NO)-N-15-O-18 in N
O products and 50% (NOO)-N-15-O-16-O-18, 25% (NO2)-N-15-O-16, and 25%
(NO2)-N-15-O-18 in NO2 products. In the absence of O-2, formation of N
2O was observed at <300 degrees C but not NO2. For Cu-NaZSM-5, its N2O
products are exclusively (N2O)-N-15-O-18, suggesting that lattice oxy
gen is not involved in the formation of N2O (it is derived solely from
(NO)-N-15-O-18) and the isotope exchange between (N2O)-N-15-O-18 With
the zeolite lattice oxygen (O-16) is not significant. However, for Co
-ZSM-5, formation of either N2O or NO2 is negligible with (NO)-N-15-O-
18 treatment. Treatment in both (NO)-N-15-O-18 and O-2 resulted in som
e formation of N2O, consisting of equal amounts of (N2O)-N-15-O-16 and
(N2O)-N-15-O-18, suggesting either isotopic exchange occurred between
N2O and lattice oxygen, or between NO and lattice oxygen, or formatio
n of N2O involved lattice oxygen. Except that the low-temperature acti
vity for N-2 formation for Cu-NaZSM-5 treated in (NO)-N-15-O-18 alone
is due to formation of N2O, the majority of activity for N-2 formation
is due to formation of NO2 intermediates. The main difference between
Cu-NaZSM-5 and Co-NaZSM-5 is that for Cu-NaZSM-5, in addition to the
low-temperature activity shared by Co-NaZSM-5, it showed significant a
ctivity for nitric oxide decomposition at high temperatures (>360 degr
ees C) while Co-NaZSM-5 showed little. A TOF of 2.88 x 10(-4) s(-1). C
u-1 for Cu-NaZSM-5 at 122 degrees C and at 0.1 vol.% (NO)-N-15-O-18 an
d 0.4 vol.% O-2 is even higher than similar to 2 x 10(-4) s(-1). Cu-1
reported in the literature at >350 degrees C, but at a much lower temp
erature. In terms of Nz formation, Co-NaZSM-5 is about 2-3 times more
active than Cu-NaZSM-5 at low temperatures (<200 degrees C). For Cu-Na
ZSM-5, its activity for NO2 decomposition is approximately 4 times hig
her than that for NO at 320-370 degrees C. Co-NaZSM-5 does not show an
y significant activity for NO decomposition but its activity for NO2 d
ecomposition is comparable to Cu-NaZSM-5. (C) 1997 Academic Press, Inc
.