The redox reaction and the oxidation state of silver in a glass melt w
ere studied by cyclic voltammetry and chronopotentiometry between 800
degrees and 1200 degrees C, Silver ions in glass were reduced at a les
s noble potential than the rest potential of a platinum electrode, A r
eversible redox reaction of silver in glass was indicated from the ana
lysis of the cyclic voltammogram, An analysis based on the electron tr
ansference number revealed that the solubility of reduced silver incre
ased with increasing temperature, Ag+/Ag-o equilibrium in glass was su
ggested because the rest potential of the platinum electrode in glass
was a mixed potential, No relation was observed between the redox beha
vior of silver in glass and optical basicity. O-type redox behavior of
silver in glass was shown.