The Raman scattering and photoluminescence from a Zn0.76Cd0.24Se-ZnSe
Superlattice at room temperature and 77 K have been studied. Two kinds
of LO phonon confined modes were observed in detail for the first tim
e, they were ascribed to those of ZnSe barrier layers and Zn0.76Cd0.24
Se well layers in the superlattice respectively. Four orders of LO mul
ti-phonon modes for well layers, including Stokes and anti-Stokes, and
five orders of LO(b) multi-phonon modes for barrier layers were seen
clearly at room temperature. At 77 K every order of LO phonon modes sh
ifts a little toward lower frequency. Three photoluminescence peaks lo
cated at 2.478 eV (19990 cm(-1)), 2.554 eV( 20600 cm(-1))and 2.387 eV
(19250 cm(-1)) were observed at room temperature.