R. Garre et al., ELECTRICAL AND MAGNETIC CHARACTERIZATION OF HOT-EXTRUDED BSCCO TAPE SAMPLES, Nuovo cimento della Societa italiana di fisica. D, Condensed matter,atomic, molecular and chemical physics, biophysics, 16(12), 1994, pp. 2113-2117
Ag/BSCCO-2223 phase tapes were prepared with a new plastic deformation
cycle. Starting from the hot extrusion of composite billets, hundreds
of metres of tape 0.15 x 3 mm were obtained by drawing and rolling th
e extruded bars. The cross-section, monofilamentary with a central Ag
insert, is quite regular along all the length. Samples from 30 cm to 1
00 cm in length were heat-treated at different temperatures between 83
0 degrees C and 480 degrees C in Ar + 10% O-2 atmosphere. Electrical-t
ransport properties were tested at 77 K. J(c) of 3000 A/cm(2) were usu
ally achieved after first heat treatment. The superconducting properti
es were also tested by magnetic measurements using a vibrating sample
magnetometer.