Y. Lin et al., REORDERING, RECRYSTALLIZATION AND RECOVERY BEHAVIOR OF (CO0.78FE0.22)(3)-V AS A FUNCTION OF THE INITIAL-STATE OF ORDER .2. MICROSTRUCTURE, Journal of Materials Science, 30(11), 1995, pp. 2738-2742
Optical and electron micrography were used to examine the progress of
recovery and recrystallization in the (Co-Fe-V) alloy rolled in the in
itially disordered state and annealed at a range of temperatures, and
the results were related to the measurements reported in Part I of thi
s study, The indirect results include a plot of fraction recrystallize
d at various temperatures against annealing time: unexplained anomalou
s behaviour was found at the highest temperature. Stacking-faults and
antiphase domain boundaries in the recrystallized grains were examined
.