Y. Soutome et al., FABRICATION OF YBACUO NONSUPERCONDUCTIVE-YBACUO YBACUO COPLANAR JOSEPHSON-JUNCTION BY FOCUSED ION-BEAM/, IEEE transactions on applied superconductivity, 5(2), 1995, pp. 2624-2627
Thin film of YBa(2)Cu3O(7-delta) grown on the MgO substrate damaged by
a focused ion beam loses superconductivity due to an abnormal growth.
We have fabricated a YBa2Cu3O7-delta co-planar Josephson junction who
se coupling region is a nonsuperconductive YBa2Cu3O7-delta grown on an
MgO substrate damaged locally by a scan of a focused ion beam. The I-
V characteristic of the junction behaves like a flux how type. At temp
eratures from 4.2K to 60K, Shapiro steps were observed for the junctio
ns in which the length of the coupling region was from 0.2 mu m to 1 m
u m. The highest IcRn product of the junction was 5.0mV. The critical
current density decreased exponentially with the junction length. It i
s considered that nonsuperconductive YBa2CU3O7-delta grown on the dama
ged substrate works as a normal layer in an S-N-S junction. Also the j
unction responded to the magnetic field and behaved like asymmetric de
-SQUID.