A. Oshima et al., IMPROVEMENT OF RADIATION-RESISTANCE FOR POLYTETRAFLUOROETHYLENE (PTFE) BY RADIATION CROSS-LINKING, Radiation physics and chemistry, 49(2), 1997, pp. 279-284
Citations number
13
Categorie Soggetti
Nuclear Sciences & Tecnology","Chemistry Physical","Physics, Atomic, Molecular & Chemical
Crosslinked polytetrafluoroethylene(PTFE) was prepared by electron bea
m irradiation in the molten state of PTFE at 340 +/- 3 degrees C in in
ert gas atmosphere. The crosslinking density was changed by the irradi
ation dose. Radiation resistance of the crosslinked PTFE was examined
on the mechanical properties after gamma-ray irradiation at room tempe
rature under vacuum and in air. Dose at a half value of elongation at
break was about 1 MGy for 500 kGy-crosslinked PTFE, while dose for non
-crosslinked PTFE was only 3.5 kGy. It has been found that the radiati
on resistance of PTFE can be improved to large extent by crosslinking.
Copyright (C) 1997 Elsevier Science Ltd