The heat capacity of ErMnO3 was measured by differential scanning calo
rimetry (DSC) from 300 K to about 850 K. The heat capacity value at 29
8 K was determined to be 103.7 J mol(-1) K-1. In order to obtain therm
odynamic data at higher temperatures, the enthalpy change of ErMnO3, H
-T(0)-H-298(0), was measured in the temperature range 673-1373 K by th
e drop method. The accuracy of the enthalpy measurement was checked by
comparing the measured enthalpy changes of Er2O3 and Mn2O3 with liter
ature values. The relative error was +/- 2% for both compounds. Howeve
r, for the heat capacity calculated from the enthalpy change, the maxi
mum deviation of the heat capacity from the references was +/- 3 %. Th
e equation for the heat capacity of ErMnO3 derived by combining the tw
o methods (DSC and drop methods) was C-p = 111.9 + 26.4 x 10(-3) T-1.3
3 x 10(6) T-2 from 298 to 1373 K. The standard Gibbs free energy of fo
rmation for ErMnO3, -1362.7 kJ mol(-1) at 298 K, was also calculated u
sing the above data.