L. Lanotte et al., LOW-MAGNETOSTRICTION CO-P LAYERS WITH MIXED CRYSTALLINE-AMORPHOUS STRUCTURE PREPARED BY ELECTROCHEMICAL DEPOSITION, Journal of magnetism and magnetic materials, 125(1-2), 1993, pp. 57-63
A Co-P alloy having a mixed amorphous/crystalline structure was produc
ed by electrochemical deposition. X-ray spectra, differential scanning
calorimetry and scanning electron microscopy were performed in order
to obtain the structural characterization. A comparison of the new kin
d of material with known amorphous and crystalline alloys was also mad
e on the basis of initial magnetization curves, electrical resistivity
and standing magnetoelastic wave amplitudes. Differential scanning ca
lorimetry reveals that the amorphous component in the mixed structure
sample does not include one of the two disordered phases that are pres
ent in the completely amorphous material. The measured physical proper
ties are explained by means of the structural characteristics and the
related phosphorus content. In the new type of material a very low mag
netostriction value is predicted and its effect on the magnetoelastic
wave amplitude is demonstrated.