Rb. Grabova et al., MICROSTRUCTURAL STUDY OF AN IRRADIATED HIGH-NICKEL ALLOY BY X-RAY-LINE PROFILE ANALYSIS AND TEM OBSERVATIONS, Journal of nuclear materials, 240(3), 1997, pp. 229-235
Citations number
16
Categorie Soggetti
Nuclear Sciences & Tecnology","Mining & Mineral Processing","Material Science
The microstructure was investigated in previously deformed specimens o
f a high-nickel alloy with four levels of initial dislocation density,
both before and after irradiation in BOR-60 reactor at 370-400 degree
s C and three displacement rates. The network dislocation density, dis
location loop radius and loop number density were determined by both X
-ray line profile analysis and TEM observations. The dependence of dis
location structure parameters on irradiation conditions and initial ne
twork density was obtained.