POLY(2,6-DIMETHYL-L,4-PHENYLENE OXIDE) POLY(BUTADIENE)DIOL INTERPENETRATING POLYMER NETWORKS - PHASE MORPHOLOGICAL-CHARACTERISTICS AND GLASS-TRANSITION TEMPERATURE BEHAVIOR/

The fracture surface topography of simultaneous interpenetrating polym er networks (SIN'S) of poly(2,6-dimethyl-1,4 phenylene oxide) (PPO)/po ly(butadiene) diol was examined by scanning electron microscopy (SEM). The phase morphology of the IPNs is highly dependent on PPO/poly(buta diene) diol mass ratio. A single-phase morphology of the IPNs was achi eved when the content of poly(butadiene)diol is below 40 wt % in the i nitial composition. The SEM observations are also wholly consistent wi th the glass transition temperature behavior obtained in the different ial scanning calorimetric (DSC) measurements. (C) 1994 John Wiley & So ns, Inc.