M. Naoe et S. Nakagawa, MAGNETO-OPTICAL CHARACTERISTICS OF BAM FERRITE CO-OXIDE MULTILAYERED FILMS/, IEEE transactions on magnetics, 29(6), 1993, pp. 3393-3395
Multilayers composed of 25 bilayers of magnetoplumbite type of barium
ferrite(BaM) layers as thin as 120 Angstrom and CoO or Co3O4 layers on
ZnO/SiO2/Si substrates were prepared by vacuum-arc evaporation. X-ray
diffraction indicated these multilayers possessed clear periodic stru
cture with sharp and flat interfaces. Mossbauer spectroscopy indicated
strong magnetic interactions among the iron and cobalt ions through t
he interfaces. The apparent orientation of magnetic spins in the BaM/C
oO multilayer was parallel to the layer planes. Multilayer exhibited a
magnetic spin orientation which was oblique to the layer planes, a co
ercivity H-c of 2.0 kOe and Kerr rotation angle theta(K) of 10 min.