Fe/Cu compositionally modulated films made by rf sputtering were inves
tigated with ferromagnetic resonance. Spin wave resonances related to
interlayer exchange coupling were observed and the phase change of the
spin wave was shared by both the Fe and Cu sublayers. The effective s
pin wave dispersion coefficient was found to increase with increasing
thickness of Cu sublayers.