E. Surian et al., INFLUENCE OF CHROMIUM ON THE MECHANICAL-PROPERTIES AND MICROSTRUCTUREOF WELD METAL FROM A HIGH-STRENGTH SMA ELECTRODE, Welding journal, 73(3), 1994, pp. 190000045-190000053
In the present work, the influence of Cr on mechanical properties and
MiCrostructure of weld metal from a high-strength SMA electrode is ana
lyzed by considering 12 experimental low-alloy low-hydrogen iron powde
r AWS E10018, E11018, E12018-M type covered electrodes. These electrod
es were manufactured to obtain in the weld deposits Cr contents rangin
g from 0 to 1.8%, with two different Mn levels for each Cr content, ma
intaining the amount of other elements at a fixed value. All-weld-meta
l specimens and production-type single V-groove welds were mechanicall
y tested in the as-welded and stress-relieved conditions, and a metall
ographic study was conducted. Chromium was found to be deleterious to
toughness with only a minor influence due to Mn variations. A postweld
heat treatment led in all cases to a reduction of toughness. Increasi
ng Cr content in the welds produced, a higher proportion of acicular f
errite and a general refinement of the microstructure.