M. Yashima et al., RAMAN-SCATTERING STUDY OF CUBIC-TETRAGONAL PHASE-TRANSITION IN ZR1-XCEXO2 SOLID-SOLUTION, Journal of the American Ceramic Society, 77(4), 1994, pp. 1067-1071
A structural phase transition between the cubic (space group, Fm3m) an
d tetragonal (space group, P4(2)/nmc) phases in a zirconia-ceria solid
solution (Zr1-xCexO2) has been observed by Raman spectroscopy. The cu
bic-tetragonal (c-t'') phase boundary in compositionally homogeneous s
amples exists at a composition X0 (0.8 < X0 < 0.9) at room temperature
, where t'' is defined as a tetragonal phase whose axial ratio c/a equ
als unity. The axial ratio c/a decreases with an increase of ceria con
centration and becomes 1 at a composition X0' (0.65 < X0' < 0.7) at ro
om temperature. The sample with a composition between X0 and X0' is t'
'-ZrO2. By Raman scattering measurements at high temperatures, the tet
ragonal (t'') --> cubic and cubic --> tetragonal phase transitions occ
ur above 400-degrees-C in Zr0.2Ce0.8O2 solid solution.