Z. Kaczkowski et L. Lanotte, MODULI OF ELASTICITY OF FE80B12SI8 METALLIC-GLASS STRIPS ANNEALED TO VACUUM AT 370-DEGREES-C AND 380-DEGREES-C, IEEE transactions on magnetics, 30(2), 1994, pp. 1024-1026
Elasticity moduli at constant magnetic field and at constant induction
as the functions of magnetic bias field of the strips of Fe80B12Si8 m
etallic glass annealed in vacuum at temperatures of 370 and 380-degree
s-C were investigated. The values of moduli in as-quenched state were
changing from 133 to 155 GPa. After annealing at 370-degrees-C the mod
uli changes were from 80 to 170 GPa and after heat treatment at 380-de
grees-C DELTAE effect increased and these changes were from 60 to 170
GPa.