Jq. Jiang et al., THE STRUCTURE AND TENSILE PROPERTIES OF AL-SI ALLOY HYBRID REINFORCEDWITH ALUMINA-ALUMINOSILICATE SHORT-FIBER, Journal of Materials Science, 29(14), 1994, pp. 3767-3773
Alumina-aluminosilicate fibre hybrid reinforced aluminium-silicon allo
y was fabricated by pressure infiltration route. Tensile test results
at room temperature and at 300-degrees-C are reported. It is shown tha
t the alumina-aluminosilicate fibre ratio does have a strong influence
on the ultimate tensile strength (UTS) of these hybrid composites. At
an alumina-aluminosilicate ratio of 3:2, the optimum UTS of hybrid me
tal matrix composites (MMC) was obtained. The UTS of only alumina fibr
e reinforced MMC was improved with increasing fibre volume fraction at
300-degrees-C. No fibre,put-out was observed on the fracture surface
and longitudinal section.