Ng. Patel et al., IMPROVEMENT OF EFFICIENCY OF ITO SE THIN-FILM SOLAR-CELLS USING TELLURIUM STIMULATOR/, Crystal research and technology, 29(6), 1994, pp. 859-864
Indium Tin Oxide ITO/Se thin film solar cells have been fabricated by
Vacuum deposition. Prior to deposition of selenium film, ultrathin tel
lurium film has been deposited on ITO thin film. Tellurium film acts a
s a stimulator for bringing improvement in crystallite size, adhesion
to ITO and electrical behaviour of selenium thin films. The maximum ef
ficiency of the ITO/Se thin film solar cells without tellurium stimula
tor and with tellurium stimulator under illumination AM1 (100 mW cm(-2
)) are found to be 1.68% and 2.27% while under fluorescent tubelight (
0.15 mW cm(-2)) are found to be 5.85% and 7.05% respectively. The ITO/
Se thin film solar cells exhibits high spectral response at short wave
length The barrier height of the ITO/Se thin film solar cells was dete
rmined.