Me. Yakinci et I. Aksoy, ACTIVATION-ENERGY FOR CRYSTALLIZATION OF MELT-QUENCHED (BI1.0TL0.5GA0.5)SR2CA2CU3O10-CERAMICS(Y SUPERCONDUCTING GLASS), Superlattices and microstructures, 21, 1997, pp. 183-190
A glass of the BiSrCaCuO superconducting system with nominal (Bi1.0Tl0
.5Ga0.5)Sr2Ca2Cu3O10+y composition has been prepared by the melt-quenc
hed method. The crystallisation kinetics of the glass was investigated
using non-isothermal analysis. The activation energy for crystallisat
ion was found to be 420.6Kjmol(-1). The Superconducting transition and
zero resistance temperatures were T-c=118.8K and T-zero=114.6K respec
tively. The calculated critical current density was J(c)=8.85x10(6) Ac
m(-2) at 4.5K, In general, substitution of both Tl+3 and Ga+3 for Bi+3
increased the activation energy for crystallisation and enhanced the
superconducting phase formation. (C) 1997 Academic Press Limited.