ESTIMATED AND EXPERIMENTAL FATIGUE LIVES OF 30CRNIMO8 STEEL UNDER IN-PHASE AND OUT-OF-PHASE COMBINED BENDING AND TORSION WITH VARIABLE AMPLITUDES

Calculated fatigue lives, based on three criteria for multiaxial rando m fatigue, were compared with lives obtained from tests on cylindrical specimens of 30CrNiMo8 steel subjected to in- and out-of-phase bendin g and torsion at variable amplitudes. In the chosen fatigue criteria t he expected position of the fracture plane, determined from a variance method for the equivalent stress, were taken into account. The equiva lent stress history was related to the rain dow method and fatigue dam age was evaluated from the Palmgren-Miner hypothesis. It has been show n that the expected fatigue fracture planes agree with those determine d by experiments. The most realistic estimations of fatigue life were obtained by the criterion of maximum shear and normal stresses on the fracture plane using a modified shear stress.