Y. Moriya et al., PREPARATION OF POLYMER HYBRIDS OF THE SIO2-PVA OR SIO2-PEG SYSTEM ANDPOROUS MATERIALS MADE FROM THE HYBRID GELS, Nippon Seramikkusu Kyokai gakujutsu ronbunshi, 101(5), 1993, pp. 518-521
Apparently homogeneous transparent gels (polymer hybrid gels) were pre
pared from TEOS and PVA or PEG. IR spectra and DTA curves for the gels
and pore characteristics of porous materials obtained by heating gels
were examined. PVA incorporated into a gel seemd to be bound to the s
urrounding greater than or similar to Si-O-Si less than or similar to
network more firmly than PEG. The pore volume by N2 adsorption on a po
rous material made from the SiO2-PEG system was much larger than that
from the SiO2-PVA system. Pore size distribution curve showed that mos
t of pores in the porous material from the gel in the SiO2-PEG6000 sys
tem were about 20 angstrom in diameter, involving a little portion of
somewhat larger pores. Difference in thermal behavior between PVA and
PEG in polymer hybrid gel was discussed in terms of the difference in
the ratio of hydrophilic to hydophobic groups in the original organic
polymer.