F. Mattheis et Hu. Krebs, CONDITIONS FOR THE TEXTURED GROWTH OF Y-BA-CU-O FILMS ON ZR FOILS, Journal of alloys and compounds, 195(1-2), 1993, pp. 275-278
Y1Ba2Cu3Oy films were grown in situ on oxidized Zr foils by pulsed las
er ablation. The substrate temperature and the oxygen partial pressure
were varied from 500-degrees-C to 800-degrees-C and between 0.01 mbar
and 1 mbar, respectively, in order to determine the optimum condition
s for a c-textured growth. Particular attention was paid to the specia
l features of metallic substrates as oxidation, surface roughness, and
rolling texture. X-ray diffraction experiments and resistance measure
ments were performed in order to study the texture and the superconduc
ting properties of the films. For a substrate temperature of 750-degre
es-C and an oxygen partial pressure of 0.3 mbar a superconducting tran
sition temperature of 89 K (midpoint) was obtained.