M. Pont et al., BI-SR-CA-CU-O SUPERCONDUCTING THICK-FILMS DEPOSITED ONTO METALLIC SUBSTRATES BY PLASMA SPRAYING, Journal of alloys and compounds, 195(1-2), 1993, pp. 279-282
Bi2Sr2Ca1Cu2Ox thick layers were produced by Vacuum Plasma Spray (VPS)
on Ni and stainless steel substrates with Yttria stabilized Zirconia
as diffusion barrier and a metallic bond layer. After spraying the sam
ples were melt-textured in a gradient furnace at temperatures ranging
from 890-degrees-C to 950-degrees-C. The furnace was moved across the
samples with velocities that varied from 10 to 3000 mm/h. X-ray diffra
ction data show that the thick films are c-axis oriented and contain p
rimarily the 2212 phase. The onset of superconductivity is around 90 K
for all the measured samples while zero resistance is achieved over a
broad temperature range. The relation between the degree of texturing
and the resistance will be discussed.